Have you ever heard that cross drilled brake rotors crack? Here's the story...


Recommended Posts

Hi all, after speaking with DBA (as I need new rotors) I thought I'd ask why cross drilled rotors are only recommended for "street use" because I know a lot of people wonder why this is the case and what will suite them. The E-mail reply was as follows...

Question -

"Just one more question. I know that cross drilled are not recommend for track use, is this because of the weakening effect on the rotors or is it more a liability thing? I have heard of cracking of the discs but realistically what sort of braking are you going to have to be doing to cause this?"

Reply -

"Adam,

the reason why we don't recommend cross drilled rotors for racing or track work is due to the following:

The disc rotor face surface area is reduced due to the holes and as a result this face heats up faster under braking.

Once you release the brakes the rotors cool very quickly due to the holes.

Due to this rapid heating and cooling of the rotor face it is possible for the rotor face to sustain what is known as heat shock.

Because the rotor is unable to heat soak and dissipate heat evenly the face of the rotor can develop cracks around the holes.

The use of slotted rotors allows the disc to heat soak and cool more evenly so the rotor is less prone to suffering from heat shock.

Heat shock can be evident in cross drilled rotors even when used by an extremely energetic driver on the street. If the drivers driving style is fast with rapid jabbing of the brakes and exallerator pedals he/she will be more likely to have problems with cross drilled rotors. Due to this reason we recommend the fitting of cross drilled rotors for looks only and improved braking performance under normal driving conditions.

I hope this answers your question, but if you have any further queries please feel free to email me.

Kind Regards,

Aaron Franklin

Technical Sales Advisor

Disc Brakes Australia Pty Ltd"

Thought this might be some helpfull info!

so is it safe to assume from that that cross drilled AND slotted discs will be less prone to this?

"The use of slotted rotors allows the disc to heat soak and cool more evenly so the rotor is less prone to suffering from heat shock"

The cracks would still form around the cross drilled holes inark beacuse the change in temp would still be significant. The only way to go on the track is slotted. Do they make 5000 series for the 34 yet adz?

I failed my RWC for the first time because I had drilled rotors with 1cm - 2cm cracks on each hole nearest the edge of the rotor... they looked sweet but the funny thing was I passed my Engineerring Cert. but not the RWC.

From what I've heard the DBA rotors were drilled after they were fabricated? While the Porsche and other high-end rotors had the holes cast from factory?

Drilling post-fabrication gives less structural integrity doesn't it?

I could be wrong though..

Because they aren't $200 rotors like DBA are...

HAHA good point.

so in other words his statement is only relative to DBA rotors... not in general

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now


  • Latest Posts

    • The final part arrived today to un-clampify and simplify the intake Who would have though a 1/2" hose stainless bulkhead fitting designed for below waterline bilge pumps would be what I needed Test fit on a 3" offcut I had laying around to see if it would work, and it worked a treat All going well the intake will be on its "final version" tomorrow 
    • Good luck on the weekend mate
    • Must have been an absolute nightmare to drive when the power steer was out, the rack ratio/wheel size/caster is all set up for power assistance
    • Welcome to SAU, what are you looking at buying?
    • I checked the injectors again (1 and 2, since they’re easiest to access) to make sure they weren’t clogged. Even though the entire fuel system had been cleaned, I wanted to be certain. Everything looked clean, so I reinstalled and connected everything. When I started the car to confirm everything was okay, it immediately revved up high, so I shut it off straight away. I checked to see if I’d missed a vacuum hose or something, but everything was connected. On the second attempt, the car ran without the high idle, but I noticed a distinct “compressed air” sound coming from the engine bay. Tracing the sound, I pushed injector #6 forward slightly and the noise stopped — it turned out it wasn’t seated properly, despite the fuel rail being bolted down. While holding it in place, the car idled steadily without stalling and ran for over 5 minutes. At this point, I pulled all six injectors out just in case I hadn’t seated them correctly or dirt had gotten onto the O-rings. Unfortunately, I discovered that I had damaged 3 out of 6 injectors (the OEM 270cc ones) during installation. So yes, this was my fault. Since only the pintle caps were damaged, I’ve ordered a Fuel Injector Service Kit from NZEFI to refurbish them. In the meantime, I reinstalled my new injectors – the car now idles fine for over 15 minutes without stalling. I have not attempted to drive it so far. It’s not perfect yet, as it hesitates when the throttle is pressed, but it’s a big improvement. Unplugging the IACV with the new injectors idles at around 800rpm, even with the IACV screw tightened fully. But this is probably due to tune.
×
×
  • Create New...