hey guys

just had a another question

with the stock ceramic turbos ive heard that its impossible to know when there gona blow up but it will happen

everyone sort of says its the heat that kills them

like if ya run a bar boost or new cams etc etc

i was thinking today that maybe its the oil lines clogging up over time and blocking

leaving no oil going to the turbs and then just burning away till a ceramic explosion

what do you guys think??

or am i just talking shit

g

Link to comment
https://www.sau.com.au/forums/topic/122901-ceramic-stockies/
Share on other sites

  • Replies 64
  • Created
  • Last Reply

Top Posters In This Topic

Top Posters In This Topic

Posted Images

if you could keep the exhaust wheel and shaftat an even say 25oC, the wheel would not explode.

if its pumping 15psi @150,000rpm for 30 seconds @ 1200oC it will die fast due to expansion

if its pumping 15psi @150,000rpm for 10min @ 10oC it will stay together as long as the temps are even, and consistent

A ceramic wheel or shaft should be more heat tolerant than a steel one. Cermic pieces are fired at over 1000*C, steel won't take that. I would think that it would be the pressure of the forces pushing a ceramic shaft at very high rpm that would cause ceramic to crack, where as a steel blade will be much more tolerant than these forces.

Just my 2c.

In short,

Aim to keep those EGT's down.

What raises EGT's one engineer may ask another?

Reduced Timing

Detonation

Lean mixtures

:D

this is true, but unfortantly as you will know, the turbo relys on hot expanding gasses to operate efficiently not just gas velocity, so its a bad circle of ceramic death..lol

A ceramic wheel or shaft should be more heat tolerant than a steel one. Cermic pieces are fired at over 1000*C, steel won't take that. I would think that it would be the pressure of the forces pushing a ceramic shaft at very high rpm that would cause ceramic to crack, where as a steel blade will be much more tolerant than these forces.

Just my 2c.

And how does one bond the ceramic to the shaft.. This is where the problem lies, its not a ceramic shaft.

I was under the impression that the wheel departed the shaft because of excessive heat, which causes the material that joints the ceramic wheel to the shaft to fail.

Not suggesting that I am right, but just what I have been told.

Beat me to it. Had to have a piss while typing my post.

Edited by 09ONE_32
I was under the impression that the wheel departed the shaft because of excessive heat, which causes the material that joints the ceramic wheel to the shaft to fail.

Not suggesting that I am right, but just what I have been told.

this is half correct.

the reason is the wheel is pressed from the inside out by the shaft, and the material that bonds the wheel to the shaft weakens.

next time you flog the turbo, the wheel expands BEFORE the heat can transfer to the shaft and evenly heat the unit, causing the wheel to "fall off"

Are heat and rotating speed not related to each other?

no they aren't. boost pressure and heat are related. the higher the pressure, the higher the temp. you can increase airflow and have the same pressure and it won't raise the temp.

also having a restricting exhaust holds in the heat more. a more restricting exhaust has a higher pressure in it, which creates more heat.

At least you'll never have that problem with N1's!!

Interesting that nissan also had nylon compressor wheel and ceramic turbine wheel on the r34 GT-T.

nylon comp wheel was also for quicker spool but the main reason was for the bearings. a lighter rotating mass lightens the load on bearings, which stretched the service life!!!

:D

it was probably cheaper and lighter in wieght, which means faster response.

its like oem would be worried about how it went at 12psi for extended periods of time as this was beyond the factory scope/specs. sure they would have tried it for a few laughs, but its well within acceptable for factory configuration

One of the HPI dvds had their R34 GT-T project car blow one up on a track day but they were sort of expecting it to after all the mods they did. Was funny though.

On guy who lives near me has a NOS system on his GT-T and the stock turbo is still hanging in there.

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now



  • Similar Content

  • Latest Posts

    • That sounds like no chance of even importing one for road registering then Now I see why Duncan wants to check LHD rules for Targa...   I wonder how "bolt in" the AWD would be if you got one imported from the US and swapped it to an AUD one
    • Not to mention they drive like a bucket of bolts! yuck!
    • Ha ha ha, that's fair mate! We have the crackhead dogs now. Mainly because the missus wants the crazy dogs while she still has the energy and capacity to be able to keep up with them! Ha ha our current two are both Working GSD, there brothers and sisters (from the same litters) are in Police, Corrective Services, and I believe one did end up in defence force too. They're wild and fun, yet right now, both curled up asleep on the lounge room floor while we watch some TV. Mal is very likely the next dog (unless I get my couch potato guardian dog 😛 )   What are your Kitties names? Are you planning some house work, like those high kitty shelves, built in scratching post, and some cat passages from one room to another room?
    • Maine Coone, did look at but to big and fluffy As for performance dogs, we had Mals at work, performance dogs are fun to watch, but, way to much work for this old rooster
×
×
  • Create New...