I purchased 2 turbos off Doughboy recently that had been rebuilt by Precision turbos in Sydney.

When I got the turbos to me they looked fine, booked it in down at the workshop and my mechanic rang me a few hours later and said he had some bad news. Said both turbos had a hairline crack on the exhaust side where the actuator lid open/closes, on the surface and also down into it.

I asked for my money back but later got an email saying he had rang both Precision and GCG turbos and both workshops apparently said that is normal and they wont get any bigger, and wont affect the performance of the turbos as the lid seals the flow.

My mechanic also said he rang 4 people and 2 said its normal and will be ok, and 2 said they wouldnt go near em.

My mechanic said he could weld the break and grind it back etc, but being cast iron and always moving/changing temps he said it would just cause a crack next to the weld anyway.

End of the day DoughBoy wasnt going to give me my money back so I have no choice to fit them anyway, but what i want to know is will they be ok and will they be ok for a long time, or will the cracks eventually split too big and be forced to fix them up?

I thought it was strange a turbo workshop that apparently charged $2000 to rebuild the turbos didnt even bother fixing the cracks in the first place...

Has anyone had any experience with this sort of shit happening on turbos?

If 4 out of 6 people say they will be all right? Unless your mechanic is a ticketed welder then id say do not weld them.

If your mechanic has experience with welding housings, then he is your mechanic. But id be worried about the type of welding he is doing, the wire/ he is going to use, will be gouge the welds, how will he know what is sufficient penetration etc etc???

Having fair a amount of experience with boilers/burners and all the cast items used in these, its not unusual for castings to have what appears to be hairline cracks on the surface of their bodies. If you have to look twice to see the cracks then i think you are in the clear.

Sure the things get hot, but they are not under any mechanical load or under pressure. So the cracks will stop and grain boundaries and not propogate thru the whole casting...that would be considered catastrophic failure...and according to the calcs you can punch for cyclic heat loads would be akin to winning lottery ... not going to happen in this life time.

If you rang a place like AMEC, (materials science/testing experts) i reckon they will tell you what i have told you, but charge you coinage for the test to verify what they would be pretty sure of. Hell if you want it tested but dont require any NATA certificates for it, they will be able to confirm what 4 out of 6 people have told you, and what i suspect based on experience in the pressure piping/vessel industry.

Hope that helps?!?!?!

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now


  • Similar Content

  • Latest Posts

    • ok so if i wanted to go 18's i would go for 8's  in front 30+ or 32+ off set at front and the back 9 would be ok? what offset should i aim for.. then can i do some  hunting for wheel rim choices..    If i get this - will this fit all around: Size: 18 x 8.5 +37 - n what tyres size tyre should i get for front n back?  
    • Absolute f*cking nightmare. I had to take breaks constantly, and I was always pissed off when I got home. The line split in Italy on day 2 (we drove from the Netherlands), lol. Driving any narrow European town was... well, sh*t.   Appreciate it man. Here, I'll just drop a favourite from the load I took on Saturday.   I'll update here when things happen with the car, the thing is, with stock power and almost everything chassis-wise taken care of, there really are no problems. 268,000kms now and counting.  
    • Ah! I actually managed to snag a lightly used set.... that aren't so suitable for me right now. They don't work on a GTT without some cutting or creative heat moulding. I thought about reselling them myself cause I didn't want to murder them, but it looks like I'm probably going to attempt to murder them/melt them because I may as well. @GTSBoy @PranK can somebody close this thread?
    • Hey mate,  I have a set, one is slightly damaged but wont be noticable once installed.  Shoot me a message if your still after them 
    • I couldn't wait But, the black constant tension hose clamps were too thick and there wasn't enough clearance at the T/B and I couldn't get it to seat properly, so I had use a silver one there I also added some 3" silicone over the alloy bit that goes through to hole on the radiator support as it looked like it was sitting on the edge of the hole in the radiator support, I never noticed a rattle or anything, but there was a witness mark It is basicly done, and I can live with the silver hose clamp at the T/B, I will get a black clamp for the head vent though where it is attached to the bulkhead fitting  It never stops...LOL, only issue now with the shock tower brace is it slightly touches the under bonnet liner now, if I leave it it will either wear some paint off the brace where it touches, or damage the liner, so I removed the liner to see what I have to work with, with the liner removed I have about 20mm of clearance, but sadly the middle part of the underside of the bonnet is only dusted with paint and looks crap, so I cannot have that, but.... as I have a roll of Carbuilders premium under bonnet insulation in the garage laying around that is only 5.5mm thick (we were going to use it on the boys Patrol, but he crashed the front of it a few months and it was written off, hence why he now drives my old Honda Accord Euro), I'll use the OEM liner as a template and get the Carbuilders stuff fitted up to cover that dusted paint up
×
×
  • Create New...