lol smells like a spam bot (seeing as he has the brand name he mentioned in his nick), but oddly its on topic and in the right section. haha has me second guessing. My guess is its a way to get Google search results hits when someone searches for "welding aluminium with a mig".

but back on topic, I'm thinking of buying a MIG, but wanna be able to do aluminium welds too. do I have to get one that's capable of really low voltages as the aluminium I wanna weld is pretty thin?

Shan, same smell i got from it haha - the thing that gave it away most was the automated template used, that worked on the other thread in the US

Alloy welding requires more amps than mild steel, but as VB- stated nylon liner is best practice along with the correct gas shield- depending on the mig you get, you could get a spool gun for it that holds the roll on the gun to stop binding in the gun.

so what are YOU doing on a US based Z forum craved? good tech/fab sections on there or anything?

can you still get those push-pull guns? havent really seen em around (bar the ancient ones floatin round the shop/at trade school)

I can weld down to 1mm fillet and butt welds at work, but that is on WIA 450 industrial machines with a 'softarc' setting. But that setting my only be an Incat program.

At home, I have a WIA 175 which I weld mild and ally with. Coiled steel liner for steel, nylon for ally. Use .9mm or 1.0mm ally wire with Argon gas, no mixes, just Argon.

Did I mention my trade is Aluminium welder / fabricator?? *lol*

Cheers, Greg.

  • 4 weeks later...

as above!! use pure argon and nylon liner. the liners usually dont last that long tho

i welded heaps of alum with mig but nuthin under 4mm plate

i would say a mig weld that thin would sit on top of the metal more than a tig weld which tends to "sink in"

that was my experience. btw i was using .9 and it welded 4mm up just fine

was on a unimig 165.

  • 2 months later...
I can weld down to 1mm fillet and butt welds at work, but that is on WIA 450 industrial machines with a 'softarc' setting. But that setting my only be an Incat program.

At home, I have a WIA 175 which I weld mild and ally with. Coiled steel liner for steel, nylon for ally. Use .9mm or 1.0mm ally wire with Argon gas, no mixes, just Argon.

Did I mention my trade is Aluminium welder / fabricator?? *lol*

Cheers, Greg.

how do you go welding steel with pure argon ive never tryed it but from what ive herd it doesnt penetrate really good if it works well i would love to no as ive got a mig and i just bought a tig and really dont want to have 2 bottles

thanks tim

  • 3 weeks later...
  • 1 month later...

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now


  • Similar Content

  • Latest Posts

    • It would be different if the sealant hadn't started to peel up with gaps in the glue about ~6cm and bigger in some areas. I would much prefer not having to do the work take them off the car . However, the filler the owner put in the roof rack mount cavities has shrunk and begun to crack on the rail delete panels. I cant trust that to hold off moisture ingress especially where I live. Not only that but I have faded paint on as well as on either side of these panels, so they would need to come off to give the roofline a proper respray. My goal is to get in there and put a healthy amount of epoxy instead of panel filler/bog and potentially skin with carbon fiber. I have 2 spare rolls from an old motorcycle fairing project from a few years back and I think it'd be a nice touch on a black stag.  I've seen some threads where people replace their roof rack delete with a welded in sheet metal part. But has anyone re-worked the roof rails themselves? It seems like there is a lot of volume there to add in some threads and maybe a keyway for a quick(er) release roof rack system. Not afraid to mill something out if I have to. It would be cool to have a cross bar only setup. That way I can keep the sleek roofline that would accept a couple bolts to gain back that extra utility  3D print some snazzy covers to hide the threaded section to be thorough and keep things covered when not using the rack. 
    • Probably not. A workshop grade scantool is my go to for proper Consult interrogation. Any workshop grade tool should do it. Just go to a workshop.
    • In my head it does make sense to be a fuel problem since that is what I touched when cleaning the system. When I was testing with the fuel pressure gauge, the pressure was constantly 2.5 bar with the FPR vacuum removed. When stalling, the pressure was going up to 3.0 bar (which is how it should be on ignition).
    • ECUtalk pages don't mention they support the ABS computer (consult port has more than one CAN), so you might just need a different scan tool. But, I would expect ABS is a different light to the brake warning/handbrake light, do you see an ABS light come on for a few seconds when you turn the key from ACC to IGN? But since you said: I'd have a look at the ABS sensors in the rear hubs to make sure they are not damaged, disconnected etc.
    • OK, if it idles at 1000+ with the AAC, its not an idle airflow problem. The cold start valve just gives extra air when the engine is cold, but you have enough air without it to idle at 1000. I think you are back to a fuel problem, sorry. Can you see the fuel pressure staying constant or does it drop as the revs drop to a stall?  
×
×
  • Create New...