Okay guys, decision time! I have searched with no results….

Powder Coating Vs Anodizing

1. Which is better?

2. Which last longer?

3. Which will act better as a heat “radiator”?

4. Which will be less restrictive for airflow and not clog up the fins?

Any further info would be great!

Regards,

Sarkis

From what i have read up so far:

Anodising is "staining" the aluminium surface at a thickness of approx 0.3 - 0.5mm therefore not affecting its thermal properties.

So looks like anodising is the way to go...

Would really appreciate you opinion guys!

Regards,

Sarkis

As I said before, paint is an insulator, but radiator paint is designed for the job so if you must paint use that. Anodizing is no problem.

Powder coating - you may as well just go back to stock IC or blow up your engine now.

Thanks guys! I have also read that anodising can damage the IC fins due to the sulfuric acid wash.. is this true?

Would radiator paint fade/flake off the polished parts of the IC?

Regards,

Sarkis

I have painted my intercooler black and can't see it making bugger all difference to it's efficiency if done sensibly. I masked up the rear of the cooler and the sides of the end tanks and only painted the front so it looks stealth but still allows the majority of it's surface area to be free of paint.

I bought good quality etch primer and matte black acrylic paint and laid a very light coat of each on the front of the core and end tanks. The primer was just to try and guard against stone chips etc. By masking the entire rear of the core you stop the majority of paint being passed through the core and coating the cooling fins. My cooler still works great.

Thanks for the replies... i wanted to get my FMIC black for the stealth look rather then performance or cooling gains... so far it seems that a VERY light coat of radiator paint or Anodising is the way to go...

Got any pics please krizza_ca18det?

Cheers

I would also be concerned about the durability cause a stealth black intercooler with stonechips/flaking paint will look very shit house and cheap. Would a black mesh insert over the intercooler be a better option and also guard against said stone chips?

Yeah ring around and get a few prices. You have two options in getting it anodised or that radiator paint. If anodising doesnt wreck the fins or look patchy that seems the best option as it wouldnt stone chip. Let us know what prices you come up with for both as im going to get mine done as i prefer the stealthy factory look.

Here are a couple of pics I took of my cooler this arvo. Only one small stone chip after a year of use ( but plenty of bugs! ). I don't have any pics of my mates cooler but it doesn't look too bad. I can't help you with a price either, as his uncle owns an anodising business so he got it done for free.

post-4094-1169200406.jpg

post-4094-1169200626.jpg

Sarkis have you seen the avo ones

http://www.avoturbo.com/avoshop/product_in...products_id=241

They make them in black and they use the existing intercooler lines. Easy installation. I will show you my stealthy kit next time.

anodising is so thin it is measured in microns. The longer they leave the item in, the thicker the anodising. Anodising is one of the most hard wearing and durable surface coatings you can possibly do. The intercooler would probably want 5-20 microns, BUT with some anodising on aluminium you get a very Cloudy/ Patchy finish, and can look quite bad.

If you choose to paint it, i would recommend using a thin first coat of etch primer. You can use any automotive paint/laquer on it, heat wont be a problem.....

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now



  • Similar Content

  • Latest Posts

    • Sorry to hear your HFM BM57 was faulty,  did you contact HFM I would hope they would be at least grateful for the information if there was some sort of manufacturing fault, you would hope they would be sympathetic even if your item was 2 years old if it had never been fitted. May I ask where it leaked from ?
    • Cats are called Bella, and Donna...  Like that poisonous plant And I remember your 2 monsters, I remember making a little bit of wee when you let them out... LOL I have already installed cat doors into the laundry where their kitty litter is, and the sun room, apart from the cat doors there's not going to be any permanent mounted stuff on the interior walls (interior doors are cheap and easy to replace) I will get a outdoor cat cage thingie once I finish the landscaping out back... https://catnip.com.au/ The only off limit areas are the main bedroom and the gym room....but, currently the cats are curled up in bed, in the main bedroom with the Mrs.....LOL, the off limits for the kittens to the main bedroom lasted about 5 minutes with Jackie I currently only have 1 free standing huge cat tree multiple level scratching post thingie in the lounge room, but, I will be getting another one soon now that I'm happy with the furniture layout in the back room and have a perfect spot for it  
    • All of this is making it seem clear that running the Coppermix twin was definitely the way to go, especially in hindsight with how insane tariffs have gotten and the strength of the USD vs yen at the time.
    • That sounds like no chance of even importing one for road registering then Now I see why Duncan wants to check LHD rules for Targa...   I wonder how "bolt in" the AWD would be if you got one imported from the US and swapped it to an AUD one
    • Not to mention they drive like a bucket of bolts! yuck!
×
×
  • Create New...