I've cracked a rear DB4000. Using Ferrodo DS2500 pads.

I was at the track and the only thing apart from running it around there that I can think of as relevant is the fact that I left the track at some speed then sat in the kitty litter for 10 minutes.

Link to comment
https://www.sau.com.au/forums/topic/139840-what-causes-rotors-to-crack/
Share on other sites

I've cracked a rear DB4000. Using Ferrodo DS2500 pads.

I was at the track and the only thing apart from running it around there that I can think of as relevant is the fact that I left the track at some speed then sat in the kitty litter for 10 minutes.

Welcome to my world. My rear rotors cracked on my GT-R. I was only (At the time) using Bendix Ultimates on the rears & was always careful to let the rotors cool properly.

Did the cracks you have in your rotors start from the small return grooves on the outer circumference?

IMHO, the best bet is not to use these rotors...... :)

post-5134-1161561217.jpg

I've cracked a rear DB4000. Using Ferrodo DS2500 pads.

Here's some wild speculation that someone will probably shoot down as BS, but i read somewhere that the thermal conductivity of the pad is an important property in brake operation as it helps even out the temperature on pad and rotor. After frying my front rotors (just warped, no cracks and a blue tinge on the outer of the mating surface) with DS2500's i'm speculating that perhaps they dont conduct heat well and therefore are tougher on rotors than other pads. The outer edge of the rotor gets a lot hotter than the inside edge and the difference in thermal expansion cracks the rotor.

About 4000s - http://www.dba.com.au/DBA4000series_specs.pdf says "motorsport applications and premium street performance" for the slotted (not drilled) rotors, but in the box comes a note "warrantee of DBA product is void when used in any form or motorsport" - tossers! Since they've said motorsport applications, i can see why you cant return them based on the Fair Trading law's requirement that goods are 'fit for purpose'. That law overrules anything the manufacturer says.

Another thing about 4000s - the vane design appears to have been make to look "wikkid" rather than provide optimal cooling...but maybe i'm just bitchy.

Rgs,

Kot

Other then warming up and coolign them down...looks to be a metallurgy thing.

My old DBA 4000s lasted for years, in fact they are still going on a friends car. The 4000s i have now have the same slots as in djr81's photos...and i honestly dont hold out much faith that they will last as well as my old set (Old set had different slots arrangement)

yes vane design i think is another point. I would much prefer a nice, conventional curved vanve rotor to the k-paw DBA style, but finding one for a good price is not easy.

Wonder if the K paw idea is causing these cracks?

If you look down the inside of the rotor you can see a straight path inbetween the K paw sections that joins both sides of the rotor together. Not sure if it would cause the problem but if you add the heat that a good track session will generate this just has to be the weakest section.

If you look at a curved vain type design the vain all over lap so there is none of these straight line oportunites, I did in the end crack my RDA k paw rotors, but only after the worse possible treatment, and they cracked in the straight line area right between any of the k paw connections.

They generally recommend you have a cool down lap to help disipate air through the rotors, and naturally cool them.. instead, you quite *possibly* could have been slamming the hell out of the brakes at the last second and then came to a complete stop and suddenly cooler. So just metal fatigue?

my front rotors have 100000 hairline cracks in them. they going to go bang soon so i gotta do something about them

Try getting the cracks machined out. Even though the material will be thinner, it will be stronger as the stress will be spread out across the surface rather than being concentrated at the head of the crack. That's the theory at least.. (and why slots are curved - no corners for stress to concentrate in).

Edit: Here's what DBA has to say about rotor longetivity http://www.dba.com.au/tech/major_considerations.asp

Rgs,

Kot

Edited by MrKotter

Good old DBA's. I know quite a few people that have cracked DBA rotors.

I did that the above at EC. I came off a pretty heavy session (playing chase car to a MX5) and forgot to do a cool-down lap before bringing it into the pits.

That said, I think it was cracked when I was driving down pit lane to my garage (had a weird pulsing coming through the brake pedal), so parking it without a cool-down lap may not be the cause.

Nope always do 2 cool down laps without touch brakes if i can help it, set the stop watch at the time we leave the garage and start the cool down laps at 15 minutes.

And i have 2 ducts to each front wheel so i know they are getting plenty of air to cool them, i didnt have any brake fade and i didnt feel the pulse from the crack until the next day after getting it home. Still it would have to be stronger with the curved vain design as it would have to crack the vain as well as the rotor which is not the case with the K paw design.

so no one has heard of the dont leave your car in the same spot for longer then a few mins after coming off the track after a race. Need to move the car a few inches forward or back so the heat isnt concentrating on the same spot of the rotor. Id say you came off possibly after breaking or breaking while coming off and then sat in the litter for however long with the breaks stuck on the same spot and it was too much concentrated heat.

Sure, leaving the caliper pistons and pad parked in the same spot of the rotor when they are glowing isnt good. It will liekly warp a rotor, but i cant see it cracking them...as its a localised thing.

Crackign a rotor suggests a metallurgical flaw, or thermal shock and cyclic loads. So it would be more likely the fact that you have stone cold rotors and you roick up to the first 6 corners standing on them rather then bringing them up to temp geradually on your warm up lap as your tyres come into their working temps/pressure.

Likewise, if you come and park it glowing red/smoking then the parked pad may cause the rotor to warp, but crack? Im not sure. Perhaps the differential expansion in the rotor cause the crack, as differential expansion/contraction are a classic for it???

Well I do proper warm ups and proper cool downs.

I think the DS2500's seem to heat the rotors more. I've had people say my front rotors were glowing hot but with 2 track days on these pads and rotors, why aren't the front ones cracked? They would surely get a hell of a lot hotter.

I don't see how you can blame the pads.

Firstly, the metal in the rotor will be massively more conductive than the pad material (Any pad material).

Secondly the amount of heat input into the rotor will be defined by how hard you are braking, not by the pad characteristic.

Lastly, we are talking about rear rotors here. Mine don't usually get hot enough to flash off the high temp thermo paint (The third of the three colours). But they still crack.

And yeah, the DBA (lack of) warranty is piss week. The things are designed for track work but as soon as you get within 100 miles of a circuit the warranty is void. That is not that suprising, but it is still rubbish. I have had to bin rotors with no more than a few tenths of a mm wear. Which pisses me off no end.

Edited by djr81
I don't see how you can blame the pads.

Firstly, the metal in the rotor will be massively more conductive than the pad material (Any pad material).

Cant argue with that.

Secondly the amount of heat input into the rotor will be defined by how hard you are braking, not by the pad characteristic.

If you look at it from an energy perspective, the pad can either transfer the energy into heat or new surface area - ie by wearing out either the rotor or itself. My porsche was roughly equivant to my skyline and never had any brake issues after getting decent fluid and EBC Greens. The GTR is struggling, so next thing i'm trying is the 324mm UAS rotor kit and i'll run some ducting as well. If that doesnt work i'll try the Greens on it.

And yeah, the DBA (lack of) warranty is piss week. The things are designed for track work but as soon as you get within 100 miles of a circuit the warranty is void. That is not that suprising, but it is still rubbish. I have had to bin rotors with no more than a few tenths of a mm wear. Which pisses me off no end.

So what do you reakon is the answer? RDA? Nissan? (is nissan exy?) Upgrade?

Rgs,

Kot

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now


  • Similar Content

  • Latest Posts

    • Seat of the pants assessment of the new intake: The car is way less "doughy" when hitting the loud pedal, especially off idle when stopped or in traffic, I did use a cheapo lazer thermal thingo to measure the temp around where the pod filter got its air, it was between 55 - 60°C, in saying this the car was shut off and not moving, so the OEM intake pipe was not supplying any fresh air to where the pod was when the car was at least moving A weird bonus was induction noise on the throttle in the cabin increased a bit,  I was worried that I was actually going to lose some of that induction noise I love so much, outside though, when I got the daughter to do a WOT drive by pass for me, the induction noise has increased alot when on the throttle, not quite ITB doort, but well up there I'm extremely happy with the results and have been exploring the country roads in the region  As for house mods: 1.New front fence is up and is awesome, it really upgraded how the joint looks from the street, and the added security is nice 2. Electricians have replace some interior lights, and with more lighting in the garage, a few new motion detecting lights out the front above the garage, front room, and at the front door, which I have already found heaps helpful coming and going, also now has fancy pants CCTV all round the house The only hold point for power though is the solar and batteries due to supply issues, although this will happen over the next few weeks 3. I have done a heap of landscaping out the front and I'm almost ready to do a new small retaining wall with some nice blocks to replace the brick and cemented in rocks around the raised garden beds cemented in river stone "was the fashion at the time" the house was built. I currently have a pallet of retaining wall blocks and 2 bulka bags of 20mm blue metal to replace the wood chip that is in the raised garden beds around the house 4. I now have 3 big raised garden beds for out the back to grow some vegetables, about 70cm high, 200cm long and 100cm wide 5. My 2 compost bins are already pretty full with brown, green and kitchen waste from the landscaping I'vedone so far, but they will probably take a few months to break down, so anything else that gets chopped, trimmed, and kitchen waste will just start filling the base of the raised garden beds to about 30cm before I start throwing 40cm of good compost, and stuff, for the vegetables to grow in, I'll need a few ton of compost and soil, but the local supplier can sent me bulka bags of the stuff Basically the logs, wood chips and a few strategically placed rocks for drainage, will give the beds some good organic materials down low to break down over time, and they will hold moisture during the warmer months to save the water in my big arse water tank if we don't get alot of rain So, all in all, the car and house mods are going well, and I'm really enjoying being retired, I sleep in too 0700 and slowly plod around inside until I feel like actually doing anything, and only work in the yard for as long as want, which has actually been alot over the last few weeks,  although when you look at it, it seems that not a huge amount of work has been done,  until I look at the before I started the work pics Happy days and good times indeed 
    • hahaha yeah. Plan is to get side skirts and probably just rear pods. But going to do them one-by-one. I've got a set that I really like from RHDJapen, but that one isn't shipped to AU. So need to find someone who can get it for me
    • Here's an idea, answer the questions I asked you as they are trying to work out WHY the LSD will be binding up in a straight line.
    • You haven't driven many modern cars then have you? Most of them have sfa steering feel with their stupid electric bullshit steering systems.
×
×
  • Create New...