Hi Everyone

I'm aware there are aftermarket options but I have a question regarding the material and modification of the factory RB26 fuel rail.

From what I have gathered from various resources, if I cut and weld a stainless fitting on the end I will burn the zinc coating off and expose the steel. Now we know E85 is a bitch when it comes to corrosion. Once the zinc coating is burned off I'm guessing it would start to rust internally.

I want to weld -6 JIC male fittings onto either end. This will allow me to mount a Turbosmart 1200 reg in the factory position, feed it from the back, and remove lots of line and just keep it stock and tidy.

Can a few people clarify this for me please?

Also, can Zinc coating be reapplied?

Just found these guys in the same state. Might be the go if I decide to do it this way.

Question is, super Zinc or Nickel? haha.

http://www.zincplating.com.au/super-zinc-sa-5

http://www.zincplating.com.au/electroless-nickel



You guys must think I'm mad....


I did the same thing to my steel VQ rails, tig welding 6an stainless fittings to the end. Been there over 6 years now running e85 daily.

I think e85 has had a very hard time breaking into the market with all these myths to overcome...

  • Like 3

Everyone. Everyone says that E85 destroys everything.

lol, f**k the way some people talk it sounds like it's going to end humanity ... ahaha

I just love the extra HP

Everyone. Everyone says that E85 destroys everything.

lol, f**k the way some people talk it sounds like it's going to end humanity ... ahaha

I just love the extra HP

Illuminati, big pharma, oil barons... No it's probably just the bogan majority that want us to stop beating their V8's. :P

Everyone. Everyone says that E85 destroys everything.

lol, f**k the way some people talk it sounds like it's going to end humanity ... ahaha

I just love the extra HP

It destroys your bank account and relationships, potentially a divorce too.

  • Like 1

Zinc and nickel coatings can be reapplied. Most chroming places can do it for you. Internally its a bit tricky but can be done, externally it is easy.

Strange, why??? Nickel coating is not as good an idea cos it can flake and splinter off [like chrome]. But bright zinc doesn't do this [just check out a thousand thousand thousand bolt heads]. I used to use a guy in Punchbowl Sydney for my bright zinc......I haven't done any for a while though, I'll see if I can't dig the contact details out.

And BTW, they strip the original zinc coating off in an acid bath first then they re apply it in the electroplate bath.

Here:

http://www.agplating.com.au/

I get all my bolts and brackets done for my restored and modded Triumphs done here, so old stuff that was second hand and needed some care etc.

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now


  • Similar Content

  • Latest Posts

    • Meh, I think we're well into a new era of 90s JDM car. The days when spare engines and parts were cheap and plentiful are long gone. Therefore the YOLO approach is now massively difficult to justify, use and maintain. One should start to ponder whether an 800HP build is really justified, using stock parts. My thoughts? If you like/love the car and want to keep it and don't want to ruin yet another one, then be discrete about how much you ask from the stock parts. A 5 or 600 HP build is still a very fast car. If you want to go silly, have to have the 1000HP territory, then just drop all your cash, buy billet everything (or PRP cast block, etc etc) and use a bigger/more modern gearbag, and put a massive retrofit diff and axles into it. If you ruin any of those things then you're either ham fisted and deserve it, or you're pushing waaaay too far for the stock stuff anyway. The (presumably) young guys who are buying 30-35 year old busted arse Jap refugees and thinking they can live the life that was lived by others 20 years ago are deluded. Expectations need to be adjusted somewhat.
    • Just don’t be silly enough to think it’ll never happen either 
    • I take it that you bought the centre to suit the GTR axles? As in there was a plan, not just somehow lucky that it worked? It all looks excellent, by the way.
    • New engine block time. Up to you whether you want to keep going down this road with this project. Unfortunately a lot of these cars are like this. The road to getting these cars into decent shape is long and not fun for reasons that you're discovering. 
    • Essay time. First things first, an RB running stock turbo and boost levels shouldn't get so bad as to stall from reversion if the recirc valve has been deleted. Should get a little fluffy and annoying, but in my experience, not so bad as to stall. Of course, every car is a bit different, so it remains possible that stalling will happen. So, running with no recirc valve is somewhat of an option, for otherwise stock stuff. Atmo BOVs cause all sorts of shit, even on an otherwise stock setup. Only gets worse the higher the boost and the bigger the turbo. At that point you really need to go for a different ECU and no AFM. Rebuilding the stock recirc valve configuration is not hard. You just need a stock or aftermarket BOV with the appropriate adapter for the 2 bolt flange on the back of the J pipe, and to get/make an appropriate ~1" pipe to get the air back to the turbo inlet, and to possibly modify the inlet (if it is not stock) to take the recirc pipe back in. Not hard. Just takes some cutting and welding. Putting an R35 type AFM into the car anywhere is not as simple as just buying the AFM and throwing it in. You will also need to buy the appropriate boss that will then need to be welded onto the pipe where you're installing it. You can clearly see why by looking at the photo posted above. They are not a "simple" swap for a stocker. You can't put on in place of the stock AFM. You can put one in place of the stock AFM, if you get the mounting boss and weld it to some pipe and otherwise make that pipe piece work like the stock AFM housing. Or you can buy such an adapter, either complete with the 4 bolt flange for the air box, or without, for varying degrees of work needed to then make it fit your stock airbox or some pod filter or whatever you have going on. Oh, and the R35 AFM is not plug and play. The wiring is different, but changing that is trivial. The plug is also different so you either end up repinning the original wires onto the new plug, or you just use a short adapter. If you weld a boss to the cold side pipe, the cold side pipe really wants to be 3", otherwise the scaling on the meter can get a bit weird, but whatever the pipe size, it's not as easy as just using the (fully documented in the Nistune doco) simple method for choosing R35 AFM in X" pipe size in the software, because the scaling will already be a bit different. Anyway, all of this has been comprehensively worked through on the Nistune forums, so there is full knowledge available. I would use a Link/Haltech before I would bother putting an AFM into a cold side pipe. That's a lot of effort for a bodge. Nistune is great, can work well even at fairly high power levels, but you are stuck with the limitations of it being the stock ECU, which includes needing to use an AFM, which is not always convenient for every set of modifications. You have to have a think about what you already have, what you want to have, and decide early if you'd be better off jumping ship to an aftermarket ECU. This so you don't waste time and money doing things 2 or 3 times. Never heard of ECUmaster. Sounds like a backyard operation. If there are good tuners for it where you are, and it is a solid product, then it will be fine. We're only talking about an R engine here. Back in the day they all ran on crude nasty early 90s ECUs and they were fine. You don't need a rocket surgeon's ECU to run one.
×
×
  • Create New...